Appearance	White powder
Ba/Ti Mole Ratio	0.995~1.000
Particle size distribution	D10 um=0.30~0.60, D50 um=0.50~1.00, D90 um=0.90~2.00
Specific surface area	1.5~2.5 m2/g
Moisture	≤ 0.25%
Ignition loss	≤ 0.30%
Cl	≤ 0.001%
Standard	Technical grade
Content	99%
Capacity	50MT/month
Loading port	Shanghai
Package	1kg/bag, 25kg/bag or according to the customers’ demand
Storage	Stored in the dry and ventilated inside storeroom, prevent direct sunlight, slightly pile and put down

Appearance	White powder
Ba/Ti Mole Ratio	0.995~1.000
Particle size distribution	D10 um=0.30~0.60, D50 um=0.50~1.00, D90 um=0.90~2.00
Specific surface area	1.5~2.5 m2/g
Moisture	≤ 0.25%
Ignition loss	≤ 0.30%
Cl	≤ 0.001%
Standard	Technical grade
Content	99%
Capacity	50MT/month
Loading port	Shanghai
Package	1kg/bag, 25kg/bag or according to the customers’ demand
Storage	Stored in the dry and ventilated inside storeroom, prevent direct sunlight, slightly pile and put down

Appearance	White powder
Ba/Ti Mole Ratio	0.995~1.000
Particle size distribution	D10 um=0.30~0.60, D50 um=0.50~1.00, D90 um=0.90~2.00
Specific surface area	1.5~2.5 m2/g
Moisture	≤ 0.25%
Ignition loss	≤ 0.30%
Cl	≤ 0.001%
Standard	Technical grade
Content	99%
Capacity	50MT/month
Loading port	Shanghai
Package	1kg/bag, 25kg/bag or according to the customers’ demand
Storage	Stored in the dry and ventilated inside storeroom, prevent direct sunlight, slightly pile and put down

Appearance	White powder
Ba/Ti Mole Ratio	0.995~1.000
Particle size distribution	D10 um=0.30~0.60, D50 um=0.50~1.00, D90 um=0.90~2.00
Specific surface area	1.5~2.5 m2/g
Moisture	≤ 0.25%
Ignition loss	≤ 0.30%
Cl	≤ 0.001%
Standard	Technical grade
Content	99%
Capacity	50MT/month
Loading port	Shanghai
Package	1kg/bag, 25kg/bag or according to the customers’ demand
Storage	Stored in the dry and ventilated inside storeroom, prevent direct sunlight, slightly pile and put down

Molecular Formula: BaO3Ti
Molecular Weight: 233.19
Hazard Symbols: Xn
UN Number: UN 1564 6.1/PG 3
WGKGermany: 1
PackingGroup: III
HS Code: 28419085

Molecular Formula: BaO3Ti
Molecular Weight: 233.1922

Molecular Formula: BaO3Ti
Molecular Weight: 233.1922

BaO/TiO2 mol	0.97~1.03
Particle size(D50)	1-3μ m
Fe2O3	≤ 0.1%
Na2O + K2O	≤ 0.5%
ZrO2	≤ 0.5%
Al2O3	≤ 0.5%
SiO2	≤ 0.5%
Loss on Ignition	≤ 0.5%

BaO/TiO2 mol	0.97~1.03
Particle size(D50)	1-3μ m
Fe2O3	≤ 0.1%
Na2O + K2O	≤ 0.5%
ZrO2	≤ 0.5%
Al2O3	≤ 0.5%
SiO2	≤ 0.5%
Loss on Ignition	≤ 0.5%

BaO/TiO2 mol	0.97~1.03
Particle size(D50)	1-3μ m
Fe2O3	≤ 0.1%
Na2O + K2O	≤ 0.5%
ZrO2	≤ 0.5%
Al2O3	≤ 0.5%
SiO2	≤ 0.5%
Loss on Ignition	≤ 0.5%

BaO/TiO2 mol	0.97~1.03
Particle size(D50)	1-3μ m
Fe2O3	≤ 0.1%
Na2O + K2O	≤ 0.5%
ZrO2	≤ 0.5%
Al2O3	≤ 0.5%
SiO2	≤ 0.5%
Loss on Ignition	≤ 0.5%

BaO/TiO2 mol	0.97~1.03
Particle size(D50)	1-3μ m
Fe2O3	≤ 0.1%
Na2O + K2O	≤ 0.5%
ZrO2	≤ 0.5%
Al2O3	≤ 0.5%
SiO2	≤ 0.5%
Loss on Ignition	≤ 0.5%

Synonyms : barium meta titanate; barium titanium trioxide; titanate barium(1 : 1); vk4; vk4(oxide); yv100an
Molecular Formula : BaO3Ti
Molecular Weight : 233.19
Appearance : White Powder
EINECS : 234-975-0
Product Categories : Inorganic salts,fine chemical material

Synonyms : barium meta titanate; barium titanium trioxide; titanate barium(1 : 1); vk4; vk4(oxide); yv100an
Molecular Formula : BaO3Ti
Molecular Weight : 233.19
Appearance : White Powder
EINECS : 234-975-0
Product Categories : Inorganic salts,fine chemical material

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Molecular Formula : BaO3Ti

Molecular weight : 233.19

Appearance : White crystal powder

Assay : 99%min

Name: Barium titanate
Cas:12047-27-7
Structural formula

Performance and application
Appearance: White Powder
Application: 1 Mainly used for the preparation of electronic ceramics, PTC thermistors, capacitors and other electronic components .
2 Widely used in the electronics industry, can be used to manufacture non-linear element, an amplifier medium, a computer memory device, but also a lower volume is small, the mini-capacitors capacitance is large. Materials and other components of the ultrasonic generator is also used to make.

Specification :
Property (Pure BT) Unit Test method Specification
Upper limit Lower limit
Moisture Content % 8min.at 120℃(MJ33) 0.25 0.00
LOI % 2hr. at 1200℃(LH30/13) 0.30 0.00
D90 Um PSD(Mastersizer 2000)IR:2.4 2.00 1.00
D50 Um 1.00 0.50
D10 Um 0.60 0.30
Specific Surface Area m^2/g BET(3H-BET2000-M) 2.50 1.80
A/B ratio (Ba/Ti) XRF(S8) 1.0000 0.9950

Packaging: 50 kg /drum or 200kg/ drum
Storage:Keep in the original packaging in a clean,dry,low humidity environment.

Name: Barium titanate
Cas:12047-27-7
Structural formula

Performance and application
Appearance: White Powder
Application: 1 Mainly used for the preparation of electronic ceramics, PTC thermistors, capacitors and other electronic components .
2 Widely used in the electronics industry, can be used to manufacture non-linear element, an amplifier medium, a computer memory device, but also a lower volume is small, the mini-capacitors capacitance is large. Materials and other components of the ultrasonic generator is also used to make.

Specification :
Property (Pure BT) Unit Test method Specification
Upper limit Lower limit
Moisture Content % 8min.at 120℃(MJ33) 0.25 0.00
LOI % 2hr. at 1200℃(LH30/13) 0.30 0.00
D90 Um PSD(Mastersizer 2000)IR:2.4 2.00 1.00
D50 Um 1.00 0.50
D10 Um 0.60 0.30
Specific Surface Area m^2/g BET(3H-BET2000-M) 2.50 1.80
A/B ratio (Ba/Ti) XRF(S8) 1.0000 0.9950

Packaging: 50 kg /drum or 200kg/ drum
Storage:Keep in the original packaging in a clean,dry,low humidity environment.

Name: Barium titanate
Cas:12047-27-7
Structural formula

Performance and application
Appearance: White Powder
Application: 1 Mainly used for the preparation of electronic ceramics, PTC thermistors, capacitors and other electronic components .
2 Widely used in the electronics industry, can be used to manufacture non-linear element, an amplifier medium, a computer memory device, but also a lower volume is small, the mini-capacitors capacitance is large. Materials and other components of the ultrasonic generator is also used to make.

Specification :
Property (Pure BT) Unit Test method Specification
Upper limit Lower limit
Moisture Content % 8min.at 120℃(MJ33) 0.25 0.00
LOI % 2hr. at 1200℃(LH30/13) 0.30 0.00
D90 Um PSD(Mastersizer 2000)IR:2.4 2.00 1.00
D50 Um 1.00 0.50
D10 Um 0.60 0.30
Specific Surface Area m^2/g BET(3H-BET2000-M) 2.50 1.80
A/B ratio (Ba/Ti) XRF(S8) 1.0000 0.9950

Packaging: 50 kg /drum or 200kg/ drum
Storage:Keep in the original packaging in a clean,dry,low humidity environment.

Name: Barium titanate
Cas:12047-27-7
Structural formula

Performance and application
Appearance: White Powder
Application: 1 Mainly used for the preparation of electronic ceramics, PTC thermistors, capacitors and other electronic components .
2 Widely used in the electronics industry, can be used to manufacture non-linear element, an amplifier medium, a computer memory device, but also a lower volume is small, the mini-capacitors capacitance is large. Materials and other components of the ultrasonic generator is also used to make.

Specification :
Property (Pure BT) Unit Test method Specification
Upper limit Lower limit
Moisture Content % 8min.at 120℃(MJ33) 0.25 0.00
LOI % 2hr. at 1200℃(LH30/13) 0.30 0.00
D90 Um PSD(Mastersizer 2000)IR:2.4 2.00 1.00
D50 Um 1.00 0.50
D10 Um 0.60 0.30
Specific Surface Area m^2/g BET(3H-BET2000-M) 2.50 1.80
A/B ratio (Ba/Ti) XRF(S8) 1.0000 0.9950

Packaging: 50 kg /drum or 200kg/ drum
Storage:Keep in the original packaging in a clean,dry,low humidity environment.